一、适用

特光滑硅油布，丝光棉布，风衣布，防水尼龙布，普通尼龙布，羽绒服，莫代尔，雨伞布，泳衣布以及PU皮革等。

二、外观组成及说明

◇ 外观及组成：白色(半透明)状粘稠体，聚氨酯聚合物

◇ 布氏粘度：80000~100000CPS

◇ PH值：7.0±0.5

◇ 固体含量：40%±1

三、特性

遮盖力好、高光泽、水洗牢度好、高附着力、手刮不掉，手感柔软、耐黄变、耐老化，印刷性能优，干湿擦达到4-5级（透明）。常温下保存12个月，（避免45℃以上高温或-25℃以下低温）属于环保型水性墨。（双组份）

PU048-1A高牢度防水尼龙水性墨白（耐黄变、环保型）：牢度超好，附着力强，手刮不掉，耐黄变，耐老化，环保

PU048-1B高牢度防水尼龙水性墨透（耐黄变、环保型）：牢度超好，附着力强，手刮不掉，耐黄变，耐老化，环保，干湿擦达到4-5级

四、参考配方

五、操作流程

网纱80-100目印花 → 印2-3次2刀 → 烘干、干燥 → 热处理 或过炉(150℃,3分钟)

六、注意事项

由于面料多种多样，在印花之前需要先行测试。在有涂层的布料上印花，需要测试布料涂层跟PU体系的粘结强度.。未确定情况使用或操作不当引起的质量问题本公司概不负责 。

Otherdetailedinformation

一．Substrates

smooth silicone oil cloth,mercerized cotton ,dust coat cloth,Waterproofnylon,general nylon,down jacket cloth,modal cloth,umbrella cloth,swimsuit cloth and PU leather.

二．Appearancecompositionandspecification

Appearanceandcomposition:white(translucent)viscousbody,polyurethanepolymer

Brinellviscosity:80000-100000CPS

PHvalue:7.0±0.5

Solidcontent:40%±1

三．Features

Good covering power,high glossiness,good wash fastness,high adhesion,using fingers to scrape will not off,soft hand feel,resistance to yellowing,aging,excellent performance of printing,the wet and dry rub reaches 4-5degree(clear),can be stored for 12 months at room temperature.(avoid temperature over 45℃ or below -25℃),it confirms to environmental protection (two component)

PU048-1A high fastness waterproof nylon waterbased ink white（resistance to yellowing/environmental）：super well fastness,high adhesion,using fingers to scrape it will not off,resistance to yellowing and aging,environmental.

PU048-1B high fastness waterproof nylon waterbased ink clear（resistance to yellowing/environmental）：super well fastness,high adhesion,using fingers to scrape it will not off,resistance to yellowing and aging,environmental.The wet and dry rub reaches 4-5 degree.

四．

五．Operationprocess

printingtechnology:80-100 meshscreenprinting-printing2-3times-drying-heattreatmentorheat

pressure(150℃，3minutes)

六．Note

Duetovariousfabrics,makingtestsbeforeprinting.printingonthecoatedcloths,shouldhaveatestaboutadhesionstrengthbetweencoatedfabricsandPUsystem.Usingoroperatinginuncertaincondition,ourcompanyisnotresponsibleforqualityproblem.